AlphaCast022


General Information
Category Gold
Caratage 9-14K
Color White
Color Shade Standart White
Typology Alloys For Gold
Production Process İnvestment Casting
Density [cm3] 12.88
Solidus [°C] 858
Liquidus [°C] 941
As cast hardness [HV] 184
Ingredient
  • Ag
  • Cu
  • Zn
  • Ni
  • Deoxidant
  • Grain Refiner
  • Other
Typical Applications
Open System
Closed System
General Characteristics
As Cast Grain Size [µm]
Color Coordinates
L* 87.83
a* 1.92
b* 11.57
c* 11.72
Mechanical Caracteristics
Tensile Strength (Rm) [MPa] 510
Yields strength (Rp0.2) [MPa] 353
Elongation Rupture (A) [%] 47
As cast Hardness [HV] 184
Hardness after 70% area red. [HV]
Hardness after annealing [HV]
Hardness after age-hardening [HV] 254
Casting Processing Parameters
Pre-mixing temperature [°C] 1150
Casting Temperatures Metal [°C] Flask [°C]
Thin (below 0.5 mm ) 1100 - 1150 720 - 750
Medium ( from 0.5-1.2 mm) 1080 - 1100 700 - 730
Thick (Thick 1.2 mm) 1060 - 1080 680 - 700
After casting, cooling time for the flaks is 45 minutes.
After casting, cooling time for the flaks is 15 minutes.
Sulphuric acid (%10) - 5 min - 50°C
Age Hardening Processing Parameters
Single step age-hardening treatment Temperature [°C] Time [min] Quenching Age-hardening
Age-hardening 285 100 Cooling in furnuce