AlphaCast308


General Information
Category Gold
Caratage 10-14K
Color Red
Color Shade Russian Red
Typology Alloys For Gold
Production Process General
Density [cm3] 13.05
Solidus [°C] 845
Liquidus [°C] 895
As cast hardness [HV] 165
Ingredient
  • Ag
  • Cu
  • Zn
  • Ni
  • Deoxidant
  • Grain Refiner
  • Other
Typical Applications
Open System
Closed System
Sheet Production
General Characteristics
As Cast Grain Size [µm] 700
Color Coordinates
L* 83.9
a* 7.1
b* 15.4
c* 16.96
Mechanical Caracteristics
Tensile Strength (Rm) [MPa] 485
Yields strength (Rp0.2) [MPa] 285
Elongation Rupture (A) [%] 35
As cast Hardness [HV] 165
Hardness after 70% area red. [HV] 290
Hardness after annealing [HV] 155
Hardness after age-hardening [HV] 180
Casting Processing Parameters
Pre-mixing temperature [°C] 1080
Casting Temperatures Metal [°C] Flask [°C]
Thin (below 0.5 mm ) 1010 - 1040 660 - 720
Medium ( from 0.5-1.2 mm) 990 - 1010 600 - 660
Thick (Thick 1.2 mm) 970 - 990 540 - 600
After casting, cooling time for the flaks is 15 m
After casting, cooling time for the flaks is 45 m
Sülfürik asit (%10) - 5 dk. - 50°C
Age Hardening Processing Parameters
Single step age-hardening treatment Temperature [°C] Time [min] Quenching Age-hardening
Age-hardening 300 100 Cooling in furnuce