AlphaSoft310

General Information
Category	Gold
Caratage	8-22K
Color	Red
Color Shade	Red
Typology	Alloys For Gold
Production Process	Plastik Deformasyon Ve El İşleri
Density [cm³]	16.82
Solidus [°C]
Liquidus [°C]
As cast hardness [HV]	Depends On The Amount Of Ag To Be Added

Ingredient

Ag Cu Zn Ni Deoxidant Grain Refiner Other

Typical Applications
Open System
Closed System
Press
CNC and Lathe Production
Handmade
Hollow Chain
Machine Chain
Wire Production
Production of tube from continuous casting
Sheet Production
Hollow chain Production

General Characteristics
As Cast Grain Size [µm]	Depends On The Amount Of Ag To Be Added

Color Coordinates
L*	Depends On The Amount Of Ag To Be Added
a*	Depends On The Amount Of Ag To Be Added
b*	Depends On The Amount Of Ag To Be Added
c*	Depends On The Amount Of Ag To Be Added

Mechanical Caracteristics
Tensile Strength (Rm) [MPa]	Depends On The Amount Of Ag To Be Added
Yields strength (Rp0.2) [MPa]	Depends On The Amount Of Ag To Be Added
Elongation Rupture (A) [%]	Depends On The Amount Of Ag To Be Added
As cast Hardness [HV]	Depends On The Amount Of Ag To Be Added
Hardness after 70% area red. [HV]	Depends On The Amount Of Ag To Be Added
Hardness after annealing [HV]	Depends On The Amount Of Ag To Be Added
Hardness after age-hardening [HV]	Depends On The Amount Of Ag To Be Added

Mechanical Working Parameters

Pre-mixing temperature [°C]	1030-1080
Pickling	Sulphuric Acid (%10)

Casting Temperature	Metal - from [°C]	Metal - to [°C]
Ingot Making	1060	1100
Continuous Casting	1080	1120

Reccomended reductions
Sheet - area or thickness [%]	65
Wire - diameter [%]	45

Mechanical working recommended annealing	Temperature [°C]	Time [min]
> 5 mm	660 - 700	40
1 - 5 mm	660 - 700	30
< 1 mm	660 - 700	20

Age Hardening Processing Parameters
Single step age-hardening treatment	Temperature [°C]	Time [min]	Quenching	Age-hardening
Age-hardening	300	100	Cooling in furnuce