AlphaRoyal1600
10
14
General Information
Category
Gold
Caratage
10K-14K
Color
Yellow
Color Shade
Light Yellow
Typology
Alloys For Gold
Production Process
İnvestment Casting
Density [cm
3
]
12,65
Solidus [°C]
820
Liquidus [°C]
875
As cast hardness [HV]
105
Ingredient
Ag
Cu
Zn
Ni
Deoxidant
Grain Refiner
Other
Typical Applications
General Characteristics
As Cast Grain Size [µm]
950
Color Coordinates
L*
90,5
a*
2,16
b*
19,12
c*
19,24
Mechanical Caracteristics
Tensile Strength (Rm) [MPa]
290
Yields strength (Rp0.2) [MPa]
145
Elongation Rupture (A) [%]
52
As cast Hardness [HV]
105
Hardness after 70% area red. [HV]
270
Hardness after annealing [HV]
115
Hardness after age-hardening [HV]
127
Casting Processing Parameters
Pre-mixing temperature [°C]
1050
Casting Temperatures
Metal [°C]
Flask [°C]
Thin (below 0.5 mm )
980
-
1020
660
-
720
Medium ( from 0.5-1.2 mm)
960
-
980
600
-
660
Thick (Thick 1.2 mm)
935
-
960
540
-
600
Trees without stones
After casting, cooling time for the flaks is 15 m
Stone-in-place casting trees
After casting, cooling time for the flaks is 45 m
Pickling :
Sulphuric acid (%10) - 5 min - 50°C
Age Hardening Processing Parameters
Single step age-hardening treatment
Temperature [°C]
Time [min]
Quenching
Age-hardening
Age-hardening
250
100
Cooling in furnuce
12