PRODUCTS

AlphaUni331

14
18

General Information
Category	Gold
Caratage	14K-18K
Color	Red
Color Shade	Rose
Typology	Alloys For Gold
Production Process	General
Density [cm³]	13,30
Solidus [°C]	880
Liquidus [°C]	930
As cast hardness [HV]	165

Ingredient

Ag Cu Zn Ni Deoxidant Grain Refiner Other

Typical Applications
Open System
Closed System
Press
CNC and Lathe Production
Handmade
Hollow Chain
Machine Chain
Wire Production
Production of tube from continuous casting
Sheet Production
Hollow chain Production

General Characteristics
As Cast Grain Size [µm]

Color Coordinates
L*
a*
b*
c*

Mechanical Caracteristics
Tensile Strength (Rm) [MPa]	525
Yields strength (Rp0.2) [MPa]
Elongation Rupture (A) [%]	42
As cast Hardness [HV]	165
Hardness after 70% area red. [HV]
Hardness after annealing [HV]
Hardness after age-hardening [HV]	246

Casting Processing Parameters
Pre-mixing temperature [°C]	1120

Casting Temperatures	Metal [°C]	Flask [°C]
Thin (below 0.5 mm )	1020 - 1040	650 - 680
Medium ( from 0.5-1.2 mm)	1000 - 1020	600 - 650
Thick (Thick 1.2 mm)	990 - 1000	550 - 600

Trees without stones

Stone-in-place casting trees

Pickling :

Mechanical Working Parameters

Pre-mixing temperature [°C]	1030-1080
Pickling	Sulphuric Acid (%10)

Casting Temperature	Metal - from [°C]	Metal - to [°C]
Ingot Making	1060	1100
Continuous Casting	1080	1120

Reccomended reductions
Sheet - area or thickness [%]	65
Wire - diameter [%]	45

Mechanical working recommended annealing	Temperature [°C]	Time [min]
> 5 mm	660 - 700	40
1 - 5 mm	660 - 700	30
< 1 mm	660 - 700	20

Age Hardening Processing Parameters
Single step age-hardening treatment	Temperature [°C]	Time [min]	Quenching	Age-hardening
Age-hardening	300	100	Cooling in furnuce

12 product in your basket.see product