PRODUCTS

AlphaFine707

General Information
Category	Gold
Caratage	10-18K
Color	Yellow
Color Shade	Light Yellow
Typology	Alloys For Gold
Production Process	Plastic Deformation and Handmade
Density [cm³]	11.5
Solidus [°C]
Liquidus [°C]
As cast hardness [HV]

Ingredient

Ag Cu Zn Ni Deoxidant Grain Refiner Other

Typical Applications
Open System
Closed System
Press
CNC and Lathe Production
Handmade
Hollow Chain
Machine Chain
Wire Production
Production of tube from continuous casting
Sheet Production
Hollow chain Production

General Characteristics
As Cast Grain Size [µm]

Color Coordinates
L*
a*
b*
c*

Mechanical Caracteristics
Tensile Strength (Rm) [MPa]
Yields strength (Rp0.2) [MPa]
Elongation Rupture (A) [%]
As cast Hardness [HV]
Hardness after 70% area red. [HV]
Hardness after annealing [HV]
Hardness after age-hardening [HV]

Mechanical Working Parameters

Pre-mixing temperature [°C]	1000-1050
Pickling	Sulphuric Acid (%10)

Casting Temperature	Metal - from [°C]	Metal - to [°C]
Ingot Making	1000	1050
Continuous Casting	1020	1100

Reccomended reductions
Sheet - area or thickness [%]	65
Wire - diameter [%]	45

Mechanical working recommended annealing	Temperature [°C]	Time [min]
> 5 mm	660 - 680	40
1 - 5 mm	660 - 680	30
< 1 mm	660 - 680	20

Age Hardening Processing Parameters
Single step age-hardening treatment	Temperature [°C]	Time [min]	Quenching	Age-hardening
Age-hardening	275	100	Cooling in furnuce