PRODUCTS

AlphaFine765

General Information
Category	Gold
Caratage	8-18K
Color	Red
Color Shade	Rose
Typology	Alloys For Gold
Production Process	İnvestment Casting
Density [cm³]	14,9
Solidus [°C]	880
Liquidus [°C]	895
As cast hardness [HV]	180

Ingredient

Ag Cu Zn Ni Deoxidant Grain Refiner Other

Typical Applications
Open System
Closed System
Press
CNC and Lathe Production
Handmade
Hollow Chain
Machine Chain
Wire Production
Production of tube from continuous casting
Sheet Production
Hollow chain Production

General Characteristics
As Cast Grain Size [µm]	190

Color Coordinates
L*	82
a*	7,6
b*	16,4
c*	18,23

Mechanical Caracteristics
Tensile Strength (Rm) [MPa]	500
Yields strength (Rp0.2) [MPa]	300
Elongation Rupture (A) [%]	30
As cast Hardness [HV]	180
Hardness after 70% area red. [HV]	280
Hardness after annealing [HV]	175
Hardness after age-hardening [HV]	320

Casting Processing Parameters
Pre-mixing temperature [°C]	1060

Casting Temperatures	Metal [°C]	Flask [°C]
Thin (below 0.5 mm )	1030 - 1050	660 - 720
Medium ( from 0.5-1.2 mm)	1010 - 1030	600 - 660
Thick (Thick 1.2 mm)	980 - 1020	540 - 600

Trees without stones After casting, cooling time for the flaks is 15 m

Stone-in-place casting trees After casting, cooling time for the flaks is 45 m

Pickling : Sulphuric acid (%10) - 5 min - 50°C

Mechanical Working Parameters

Pre-mixing temperature [°C]	1040-1080
Pickling	Sulphuric Acid (%10)

Casting Temperature	Metal - from [°C]	Metal - to [°C]
Ingot Making	1060	1080
Continuous Casting	1060	1100

Reccomended reductions
Sheet - area or thickness [%]	70
Wire - diameter [%]	45

Mechanical working recommended annealing	Temperature [°C]	Time [min]
> 5 mm	640 - 680	40
1 - 5 mm	640 - 680	30
< 1 mm	640 - 680	20

Age Hardening Processing Parameters
Single step age-hardening treatment	Temperature [°C]	Time [min]	Quenching	Age-hardening
Age-hardening	300	100	Cooling in furnuce

12 product in your basket.see product