AlphaFine734
8
9
10
14
18
21
General Information
Category
Gold
Caratage
8-21K
Color
Red
Color Shade
Red
Typology
Alloys For Gold
Production Process
Universal
Density [cm
3
]
12,95
Solidus [°C]
915
Liquidus [°C]
940
As cast hardness [HV]
130
Ingredient
Ag
Cu
Zn
Ni
Deoxidant
Grain Refiner
Other
Typical Applications
Open System
Closed System
Press
CNC and Lathe Production
Handmade
Hollow Chain
Machine Chain
Wire Production
Production of tube from continuous casting
Sheet Production
Hollow chain Production
General Characteristics
As Cast Grain Size [µm]
30
Color Coordinates
L*
86,7
a*
9,8
b*
14,8
c*
17,75
Mechanical Caracteristics
Tensile Strength (Rm) [MPa]
500
Yields strength (Rp0.2) [MPa]
260
Elongation Rupture (A) [%]
33
As cast Hardness [HV]
130
Hardness after 70% area red. [HV]
272
Hardness after annealing [HV]
146
Hardness after age-hardening [HV]
153
Casting Processing Parameters
Pre-mixing temperature [°C]
1050
Casting Temperatures
Metal [°C]
Flask [°C]
Thin (below 0.5 mm )
1050
-
1070
660
-
720
Medium ( from 0.5-1.2 mm)
1030
-
1050
600
-
660
Thick (Thick 1.2 mm)
1010
-
1030
540
-
600
Trees without stones
Remove the flask within 1 minute after pouring, then quench immediately in water.
Stone-in-place casting trees
Remove the flask immediately from the machine. Dip only the bottom part of the tree in cold water and keep under ventilation for 15 minutes. Quench in water.
Pickling :
Sulphuric acid (%10) - 5 min - 50°C
Mechanical Working Parameters
Pre-mixing temperature [°C]
1020-1050
Pickling
Sulphuric Acid (%10)
Casting Temperature
Metal - from [°C]
Metal - to [°C]
Ingot Making
1000
1050
Continuous Casting
1030
1100
Reccomended reductions
Sheet - area or thickness [%]
70
Wire - diameter [%]
45
Mechanical working recommended annealing
Temperature [°C]
Time [min]
> 5 mm
630
-
670
40
1 - 5 mm
630
-
670
30
< 1 mm
630
-
670
20
Age Hardening Processing Parameters
Single step age-hardening treatment
Temperature [°C]
Time [min]
Quenching
Age-hardening
Age-hardening
300
100
Cooling in furnuce
12