AlphaCast252


General Information
Category Gold
Caratage 18K
Color White
Color Shade Standart White
Typology Alloys For Gold
Production Process İnvestment Casting
Density [cm3] 14,6
Solidus [°C] 895
Liquidus [°C] 925
As cast hardness [HV] 220
Ingredient
  • Ag
  • Cu
  • Zn
  • Ni
  • Deoxidant
  • Grain Refiner
  • Other
Typical Applications
Open System
Closed System
Sheet Production
General Characteristics
As Cast Grain Size [µm] 730
Color Coordinates
L* 84,81
a* 1,57
b* 10,31
c* 10,46
Mechanical Caracteristics
Tensile Strength (Rm) [MPa] 525
Yields strength (Rp0.2) [MPa] 420
Elongation Rupture (A) [%] 30
As cast Hardness [HV] 220
Hardness after 70% area red. [HV] 320
Hardness after annealing [HV] 210
Hardness after age-hardening [HV] 235
Casting Processing Parameters
Pre-mixing temperature [°C] 1120
Casting Temperatures Metal [°C] Flask [°C]
Thin (below 0.5 mm ) 1100 - 1120 700 - 730
Medium ( from 0.5-1.2 mm) 1080 - 1100 680 - 700
Thick (Thick 1.2 mm) 1050 - 1080 650 - 680
After casting, cooling time for the flaks is 45 minutes.
After casting, cooling time for the flaks is 15 minutes.
Sulphuric acid (%10) - 5 min - 50°C
Age Hardening Processing Parameters
Single step age-hardening treatment Temperature [°C] Time [min] Quenching Age-hardening
Age-hardening 285 100 Cooling in furnuce