PRODUCTS

Brands Page

AlphaCast217


General Information
Category Gold
Caratage 9-18K
Color White
Color Shade Standart White
Typology Alloys For Gold
Production Process İnvestment Casting
Density [cm3] 13
Solidus [°C] 895
Liquidus [°C] 970
As cast hardness [HV] 185
Ingredient
  • Ag
  • Cu
  • Zn
  • Ni
  • Deoxidant
  • Grain Refiner
  • Other
Typical Applications
Open System
Closed System
Sheet Production
General Characteristics
As Cast Grain Size [µm] 150
Color Coordinates
L* 87,75
a* 2,3
b* 11,35
c* 11,58
Mechanical Caracteristics
Tensile Strength (Rm) [MPa] 672
Yields strength (Rp0.2) [MPa] 400
Elongation Rupture (A) [%] 31
As cast Hardness [HV] 185
Hardness after 70% area red. [HV] 315
Hardness after annealing [HV] 200
Hardness after age-hardening [HV] 248
Casting Processing Parameters
Pre-mixing temperature [°C] 1120
Casting Temperatures Metal [°C] Flask [°C]
Thin (below 0.5 mm ) 1050 - 1090 660 - 720
Medium ( from 0.5-1.2 mm) 1020 - 1050 600 - 660
Thick (Thick 1.2 mm) 1000 - 1020 540 - 600
After casting, cooling time for the flaks is 45 minutes.
After casting, cooling time for the flaks is 15 minutes.
Sulphuric acid (%10) - 5 min - 50°C
Age Hardening Processing Parameters
Single step age-hardening treatment Temperature [°C] Time [min] Quenching Age-hardening
Age-hardening 285 100 Cooling in furnuce