PRODUCTS

Brands Page

AlphaCast215


General Information
Category Gold
Caratage 8-18K
Color White
Color Shade Standart White
Typology Alloys For Gold
Production Process İnvestment Casting
Density [cm3] 12,7
Solidus [°C] 900
Liquidus [°C] 955
As cast hardness [HV] 152
Ingredient
  • Ag
  • Cu
  • Zn
  • Ni
  • Deoxidant
  • Grain Refiner
  • Other
Typical Applications
Open System
Closed System
Sheet Production
General Characteristics
As Cast Grain Size [µm] 680
Color Coordinates
L* 85
a* 1
b* 9,6
c* 9,65
Mechanical Caracteristics
Tensile Strength (Rm) [MPa] 605
Yields strength (Rp0.2) [MPa] 375
Elongation Rupture (A) [%] 33
As cast Hardness [HV] 152
Hardness after 70% area red. [HV] 315
Hardness after annealing [HV] 170
Hardness after age-hardening [HV] 180
Casting Processing Parameters
Pre-mixing temperature [°C] 1120
Casting Temperatures Metal [°C] Flask [°C]
Thin (below 0.5 mm ) 1065 - 1100 660 - 720
Medium ( from 0.5-1.2 mm) 1045 - 1065 600 - 660
Thick (Thick 1.2 mm) 1025 - 1045 540 - 600
After casting, cooling time for the flaks is 45 minutes.
After casting, cooling time for the flaks is 15 minutes.
Sulphuric acid (%10) - 5 min - 50°C
Age Hardening Processing Parameters
Single step age-hardening treatment Temperature [°C] Time [min] Quenching Age-hardening
Age-hardening 285 100 Cooling in furnuce