AlphaCast187


General Information
Category Gold
Caratage 18K
Color Yellow
Color Shade 2N
Typology Alloys For Gold
Production Process İnvestment Casting
Density [cm3] 15,33
Solidus [°C] 865
Liquidus [°C] 910
As cast hardness [HV] 130
Ingredient
  • Ag
  • Cu
  • Zn
  • Ni
  • Deoxidant
  • Grain Refiner
  • Other
Typical Applications
Open System
Closed System
Sheet Production
General Characteristics
As Cast Grain Size [µm] 300
Color Coordinates
L* 89,45
a* 2,86
b* 23,79
c* 23,96
Mechanical Caracteristics
Tensile Strength (Rm) [MPa] 340
Yields strength (Rp0.2) [MPa] 245
Elongation Rupture (A) [%] 44
As cast Hardness [HV] 130
Hardness after 70% area red. [HV] 200
Hardness after annealing [HV] 140
Hardness after age-hardening [HV] 205
Casting Processing Parameters
Pre-mixing temperature [°C] 1080
Casting Temperatures Metal [°C] Flask [°C]
Thin (below 0.5 mm ) 1030 - 1070 660 - 720
Medium ( from 0.5-1.2 mm) 1000 - 1030 620 - 660
Thick (Thick 1.2 mm) 980 - 1000 540 - 600
After casting, cooling time for the flaks is 45 minutes.
After casting, cooling time for the flaks is 15 minutes.
Sulphuric acid (%10) - 5 min - 50°C
Age Hardening Processing Parameters
Single step age-hardening treatment Temperature [°C] Time [min] Quenching Age-hardening
Age-hardening 275 100 Cooling in furnuce