AlphaCast186


General Information
Category Gold
Caratage 18K
Color Yellow
Color Shade Arabic Yellow
Typology Alloys For Gold
Production Process İnvestment Casting
Density [cm3] 15
Solidus [°C] 825
Liquidus [°C] 855
As cast hardness [HV] 160
Ingredient
  • Ag
  • Cu
  • Zn
  • Ni
  • Deoxidant
  • Grain Refiner
  • Other
Typical Applications
Open System
Closed System
Sheet Production
General Characteristics
As Cast Grain Size [µm] 280
Color Coordinates
L* 83,9
a* 2,8
b* 21
c* 21,2
Mechanical Caracteristics
Tensile Strength (Rm) [MPa] 300
Yields strength (Rp0.2) [MPa] 200
Elongation Rupture (A) [%] 35
As cast Hardness [HV] 160
Hardness after 70% area red. [HV] 270
Hardness after annealing [HV] 170
Hardness after age-hardening [HV] 290
Casting Processing Parameters
Pre-mixing temperature [°C] 1080
Casting Temperatures Metal [°C] Flask [°C]
Thin (below 0.5 mm ) 1000 - 1040 660 - 720
Medium ( from 0.5-1.2 mm) 970 - 1000 620 - 660
Thick (Thick 1.2 mm) 940 - 970 540 - 600
After casting, cooling time for the flaks is 45 minutes.
After casting, cooling time for the flaks is 15 minutes.
Sulphuric acid (%10) - 5 min - 50°C
Age Hardening Processing Parameters
Single step age-hardening treatment Temperature [°C] Time [min] Quenching Age-hardening
Age-hardening 275 100 Cooling in furnuce