AlphaCast119


General Information
Category Gold
Caratage 14K
Color Yellow
Color Shade Hamilton
Typology Alloys For Gold
Production Process İnvestment Casting
Density [cm3] 13,20
Solidus [°C] 810
Liquidus [°C] 860
As cast hardness [HV] 155
Ingredient
  • Ag
  • Cu
  • Zn
  • Ni
  • Deoxidant
  • Grain Refiner
  • Other
Typical Applications
Open System
Closed System
Sheet Production
General Characteristics
As Cast Grain Size [µm]
Color Coordinates
L*
a*
b*
c*
Mechanical Caracteristics
Tensile Strength (Rm) [MPa] 400
Yields strength (Rp0.2) [MPa]
Elongation Rupture (A) [%] 45
As cast Hardness [HV] 155
Hardness after 70% area red. [HV]
Hardness after annealing [HV]
Hardness after age-hardening [HV] 267
Casting Processing Parameters
Pre-mixing temperature [°C] 1050
Casting Temperatures Metal [°C] Flask [°C]
Thin (below 0.5 mm ) 980 - 1020 660 - 700
Medium ( from 0.5-1.2 mm) 960 - 980 620 - 660
Thick (Thick 1.2 mm) 930 - 960 580 - 620
After casting, cooling time for the flaks is 45 minutes.
After casting, cooling time for the flaks is 15 minutes.
Sulphuric acid (%10) - 5 min - 50°C
Age Hardening Processing Parameters
Single step age-hardening treatment Temperature [°C] Time [min] Quenching Age-hardening
Age-hardening 275 100 Cooling in furnuce