PRODUCTS

Brands Page

AlphaSoft077


General Information
Category Gold
Caratage 14K-18K
Color White
Color Shade Standart White
Typology Alloys For Gold
Production Process Plastic Deformation and Handmade
Density [cm3] 14.61
Solidus [°C]
Liquidus [°C]
As cast hardness [HV]
Ingredient
  • Ag
  • Cu
  • Zn
  • Ni
  • Deoxidant
  • Grain Refiner
  • Other
Typical Applications
General Characteristics
As Cast Grain Size [µm]
Color Coordinates
L*
a*
b*
c*
Mechanical Caracteristics
Tensile Strength (Rm) [MPa]
Yields strength (Rp0.2) [MPa]
Elongation Rupture (A) [%]
As cast Hardness [HV]
Hardness after 70% area red. [HV]
Hardness after annealing [HV]
Hardness after age-hardening [HV]
Mechanical Working Parameters
Pre-mixing temperature [°C] 1030-1080
Pickling Sulphuric Acid (%10)
Casting Temperature Metal - from [°C] Metal - to [°C]
Ingot Making 1030 1080
Continuous Casting 1060 1120
Reccomended reductions
Sheet - area or thickness [%] 65
Wire - diameter [%] 45
Mechanical working recommended annealing Temperature [°C] Time [min]
> 5 mm 660 - 700 40
1 - 5 mm 660 - 700 30
< 1 mm 660 - 700 20
Age Hardening Processing Parameters
Single step age-hardening treatment Temperature [°C] Time [min] Quenching Age-hardening
Age-hardening 285 100 Cooling in furnuce